410 Stainless Steel Strip
Stellanox Steel offers robust and reliable 410 Stainless Steel Strips, engineered for applications that demand high strength, hardness, and moderate corrosion resistance. As a martensitic stainless steel, 410 strip delivers excellent wear resistance and can be heat-treated to enhance mechanical properties, making it ideal for cutlery, valves, fasteners, and industrial blades.
It is widely used in automotive, construction, and tooling industries due to its durability, magnetic properties, and ease of fabrication.
What is 410 Stainless Steel Strip?
410 Stainless Steel Strip is a martensitic chromium stainless steel grade that provides good corrosion resistance, high tensile strength, and excellent hardness after heat treatment. It contains 11.5–13.5% chromium, giving it oxidation resistance in mild atmospheres, along with the ability to be hardened through quenching and tempering.
Supplied in annealed, hardened, or tempered conditions, it is suitable for machining, grinding, and forming operations, and exhibits magnetic properties in all states.
| Products |
|---|
|
Stainless Steel |
|
Carbon Steel |
|
Duplex Stainless Steel |
|
Super Duplex Stainless Steel |
|
Alloy Steel |
|
Titanium |
|
Hastelloy |
|
Inconel |
|
Monel |
|
Aluminium |
|
Copper |
|
Pure Nickel |
|
Flanges |
|
Forged Fittings |
|
Valves |
|
Fasteners |
Key Features of 410 Stainless Steel Strip
- High Hardness: Can be hardened through heat treatment for cutting and wear applications.
- Moderate Corrosion Resistance: Performs well in mild atmospheric and chemical environments.
- Good Machinability: Ideal for precision parts and components.
- Heat Treatable: Enables higher strength and hardness.
- Magnetic Properties: Naturally magnetic in all conditions.
- Cost-Effective: Lower cost than austenitic grades like 304 and 316.
Specification Chart – 410 Stainless Steel Strip
| Property | Details |
|---|---|
| Grade | 410 (UNS S41000) |
| Standards | ASTM A240, ASTM A276, EN 10088-2 |
| Thickness Range | 0.1 mm – 3.0 mm |
| Width Range | 5 mm – 600 mm |
| Coil ID / OD | 200 mm / 400–800 mm (customizable) |
| Surface Finishes | 2B, BA, Polished, No. 4 |
| Edge Condition | Slit Edge, Rounded Edge |
| Processing Options | Slitting, Cut-to-Length, Tempered |
Chemical Composition – 410 Stainless Steel Strip
| Element | Composition (%) |
|---|---|
| Chromium (Cr) | 11.5 – 13.5 |
| Carbon (C) | 0.08 – 0.15 |
| Manganese (Mn) | ≤ 1.00 |
| Silicon (Si) | ≤ 1.00 |
| Phosphorus (P) | ≤ 0.040 |
| Sulfur (S) | ≤ 0.030 |
| Iron (Fe) | Balance |
Mechanical Properties – 410 Stainless Steel Strip (Annealed)
| Property | Value |
|---|---|
| Tensile Strength (MPa) | ≥ 450 |
| Yield Strength (MPa) | ≥ 275 |
| Elongation (%) | ≥ 20 |
| Hardness (HRB) | ≤ 96 (Annealed) |
| Density | 7.75 g/cm³ |
Equivalent Grades
| Standard | Grade |
|---|---|
| ASTM | 410 |
| EN | 1.4006 |
| JIS | SUS 410 |
| UNS | S41000 |
| DIN | X12Cr13 |
410 Stainless Steel Strip Weight Chart
| Thickness (mm) | Weight per m² (kg) |
|---|---|
| 0.2 | 1.55 |
| 0.5 | 3.88 |
| 0.8 | 6.20 |
| 1.0 | 7.75 |
| 1.5 | 11.63 |
| 2.0 | 15.50 |
| 3.0 | 23.25 |
Applications of 410 Stainless Steel Strip
- Industrial Blades and Knives
- Pump Shafts and Valve Components
- Cutlery and Kitchen Utensils
- Fasteners and Springs
- Automotive Trim and Engine Parts
- Steam and Gas Turbine Components
- Construction and Roofing Materials
Benefits of 410 Stainless Steel Strip
- Hardenable and highly durable
- Moderate corrosion resistance in dry and mildly corrosive environments
- Magnetic and easily fabricated
- Ideal for wear-prone or mechanical components
- Cost-effective alternative to higher alloyed grades
- Excellent machinability and polishable finish